Comparative Study and Evaluation of the Compressive Strength and Mechanical Wear Resistance of Colored Geopolymer Concrete Based On Slag as a Binder
Keywords:
Concrete, Comparative study, Compressive strength, Colored geopolymer, Mechanical wear resistanceAbstract
The goal of this study is to compare the compressive strength and mechanical abrasion resistance of colored geopolymer concrete based on slag as a base ingredient. Three percentages of three colored oxides from slag were considered: 1%, 2%, and 3% of red iron oxide, green chromium oxide, and yellow iron hydroxide. In addition to a little amount of water, the combination contains a high plasticizer. According to the study's findings, the compressive strength and abrasion resistance performed best when the proportion of addition was 1% for the red and yellow colors and 2% for the green color, which generated the best results and mechanical wear resistance aluminum oxide.